specifications
 
Parameters PFG-01 VRP-M PFG-03M PFG-03C PFG-04
Holographic Sensitivity
@ 457nm CW microJ/cm2 - - - 2000 80000
@ 488nm CW microJ/cm2 - - - - 100000
@ 514.5nm CW microJ/cm2 - 75 - 3000 250000
@ 526.5nm 30ns pulse with latensification - microJ/cm2 - 75 - - -
@ 633nm microJ/cm2 80 - 1500-2000 3000 -
Maximum density on characteristic curve (Dmax) <4.0 <4.0 <4.0 <4.0 x
Resolving Power (R), mm-1 3000 3000 5000 5000 Grainless
Maximum of spectral sensitization, nm 633 530 633 457/514/633 415
Swollen emulsion layer strength after chemical processing, H (gm force) 900 900 >50 >50 x
Deformation temperature of emulsion layer in water (Tdef),oC >90oC >90oC >35oC >35oC x
Emulsion layer thickness (microns) 7 to 8 6 to 7 6 to 7 9 to 10 16 to 17
Normal diffraction efficiency for reflection holograms
@ 457nm, % - - - >25% >75%
@ 488nm, % - - - - -
@ 514.5nm, % - >45% - >45% >75%
@ 526.5nm, % - >45% - - -
@ 633nm, % >45% - >45% >45% -
Observed storage period for the holographic materials certified by Geola: at 4o Celsius, 30% humidity.
Film roll (months) 18 18 18 12 x
Cut sheets (months) 12 12 6 6 x
Plates (months) 18 18 12 12 12
 

Holography materials sizes

Emulsion coated on glass plates*
(glass thickness - 2mm)

Plate Size (mm) Q-ty per Box Box Size (mm) Box Weight
(kg)
VRP-M, PFG-01, -03C,-03M, -04 63x63 30 185x82x90 0.95
VRP-M, PFG-01, -03C,-03M, -04 102x127 25 245x168x220 3.30
VRP-M, PFG-01, -03C,-03M, -04 300x400 6 423x330x43 5.45

Emulsion coated on TAC substrate
(Triacetate substrate thickness -
180microns)

Sizes mm x m
(Roll)
Q-ty of
Rolls per
Box
Box Size
(mm)
Box Weight
(kg)
VRP-M, PFG-01, -03C,-03M 35x20 1 320x300x40 0.3
VRP-M, PFG-01, -03C,-03M 102x20 1 320x300x110 0.9
VRP-M, PFG-01, -03C,-03M 203x20 1 320x300x230 1.8
VRP-M, PFG-01, -03C,-03M 304x10 1 160x150x340 1.3
VRP-M, PFG-01, -03C,-03M 350x10 1 160x150x390 1.5
VRP-M, PFG-01, -03C** 1000x10 1 160x150x1350 8.9

* - bigger sizes on request
** - on request